Búsqueda
Inicio | Sobre Valvias | Login sponsor | Sponsor Info | Valvias Tv | Contactar | Mapa del Sitio |
Valvias El portal de Válvulas y Actuadores más visitado
  Abierto a todos fabricantes y distribuidores
[+info]  
Home contact
General
Conceptos Básicos
Tipos de Válvulas
Tipos de Actuadores
Normas y Tests
Literatura Técnica
Software
Búsqueda
Válvula
Actuador
Empresa
Empresa en Mapa
Actualidad
Peticiones de Oferta
Stocks
Artículos
Noticias
Ferias
Cursos
Ofertas de Trabajo
Utilidades
Prontuario
Glosario
Links
Valvias Tv
Login sponsor
Sponsor Info
Sobre Valvias
Contactar
Mapa del sitio
Conceptos Básicos > Diseño > Materiales English
 
Metales
Acero al Carbono Forjado
Acero Inoxidable
Acero de construcción
Fundición de Acero Aleado
Fundición de Acero al Carbono
Fundición de Dierro Dúctil (Nodular)
Fundición de Hierro Gris
Otros
Elastómero
 
Google
Coeficientes Cv Kv
Ecuaciones de fluidos
Bridas
ANSI/ASME vs ISO
Libros sobre válvulas
Fundición de Acero al Carbono
ASTMEN
A-216 WCAGS C-25
A-216 WCBEN 10213-2 1.0619
A-216 WCCDIN 1681 GS45-
Normas de fundicion de acero al carbono en válvulas

ASTM A216 / A216M - 08
Standard Specification for Steel Castings, Carbon, Suitable for Fusion Welding, for High-Temperature Service

This specification covers carbon steel castings for valves, flanges, fittings, or other pressure-containing parts for high-temperature service and of quality suitable for assembly with other castings or wrought-steel parts by fusion welding. Covered here are three grades of carbon steel (Grades WCA, WCB, and WCC), the selection of which shall depend on the design and service conditions, mechanical properties, and the high temperature characteristics. Castings shall be heat treated and furnished, as appropriate to their design and chemical composition, in the annealed, or normalized, or normalized and tempered conditions after they have been allowed to cool below the transformation range. Furnace temperatures for heat treating shall be effectively controlled by pyrometer. Steel castings shall adhere to chemical composition and tensile property requirements, which include tensile strength, yield strength, elongation, and reduction of area. The surface of castings shall be free of adhering elements such as sand, cracks, hot tears, and other discontinuities, and as such be repair welded when judged appropriate.